R60705 Alloy vs. SAE-AISI H22 Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI H22 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is SAE-AISI H22 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
77
Tensile Strength: Ultimate (UTS), MPa 540
700 to 1920

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
440
Thermal Conductivity, W/m-K 17
31
Thermal Expansion, µm/m-K 6.3
12

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.7
Embodied Water, L/kg 450
72

Common Calculations

Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 22
22 to 61
Strength to Weight: Bending, points 22
20 to 39
Thermal Diffusivity, mm2/s 9.5
8.2
Thermal Shock Resistance, points 63
22 to 60

Alloy Composition

Carbon (C), % 0 to 0.050
0.3 to 0.4
Chromium (Cr), % 0 to 0.2
1.8 to 3.8
Copper (Cu), % 0
0 to 0.25
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
82.2 to 87.4
Manganese (Mn), % 0
0.15 to 0.4
Nickel (Ni), % 0
0 to 0.3
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.15 to 0.4
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
10 to 11.8
Vanadium (V), % 0
0.25 to 0.5
Zirconium (Zr), % 91 to 98
0