R60705 Alloy vs. R31233 Cobalt

R60705 alloy belongs to the otherwise unclassified metals classification, while R31233 cobalt belongs to the cobalt alloys. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is R31233 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
220
Elongation at Break, % 18
17
Fatigue Strength, MPa 290
220
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
85
Tensile Strength: Ultimate (UTS), MPa 540
1020
Tensile Strength: Yield (Proof), MPa 430
420

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Specific Heat Capacity, J/kg-K 270
440
Thermal Conductivity, W/m-K 17
12
Thermal Expansion, µm/m-K 6.3
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.6
Embodied Water, L/kg 450
480

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
140
Resilience: Unit (Modulus of Resilience), kJ/m3 950
410
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 22
33
Strength to Weight: Bending, points 22
26
Thermal Diffusivity, mm2/s 9.5
3.2
Thermal Shock Resistance, points 63
25

Alloy Composition

Boron (B), % 0
0 to 0.015
Carbon (C), % 0 to 0.050
0.020 to 0.1
Chromium (Cr), % 0 to 0.2
23.5 to 27.5
Cobalt (Co), % 0
44.7 to 63.3
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
1.0 to 5.0
Manganese (Mn), % 0
0.1 to 1.5
Molybdenum (Mo), % 0
4.0 to 6.0
Nickel (Ni), % 0
7.0 to 11
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0.030 to 0.12
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.050 to 1.0
Sulfur (S), % 0
0 to 0.020
Tungsten (W), % 0
1.0 to 3.0
Zirconium (Zr), % 91 to 98
0