R60705 Alloy vs. S41041 Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while S41041 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is S41041 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 18
17
Fatigue Strength, MPa 290
350
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
76
Tensile Strength: Ultimate (UTS), MPa 540
910
Tensile Strength: Yield (Proof), MPa 430
580

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 17
29
Thermal Expansion, µm/m-K 6.3
10

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
140
Resilience: Unit (Modulus of Resilience), kJ/m3 950
860
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
32
Strength to Weight: Bending, points 22
27
Thermal Diffusivity, mm2/s 9.5
7.8
Thermal Shock Resistance, points 63
33

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.050
0.13 to 0.18
Chromium (Cr), % 0 to 0.2
11.5 to 13
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
84.5 to 87.8
Manganese (Mn), % 0
0.4 to 0.6
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 2.0 to 3.0
0.15 to 0.45
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 91 to 98
0