R60706 Alloy vs. AWS E3155

R60706 alloy belongs to the otherwise unclassified metals classification, while AWS E3155 belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is AWS E3155.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
210
Elongation at Break, % 16
23
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
81
Tensile Strength: Ultimate (UTS), MPa 580
770

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Specific Heat Capacity, J/kg-K 270
450
Thermal Conductivity, W/m-K 17
13
Thermal Expansion, µm/m-K 6.3
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.4
Embodied Water, L/kg 450
300

Common Calculations

Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
26
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 9.5
3.3
Thermal Shock Resistance, points 67
20

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.1
Chromium (Cr), % 0 to 0.2
20 to 22.5
Cobalt (Co), % 0
18.5 to 21
Copper (Cu), % 0
0 to 0.75
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
23.3 to 36.3
Manganese (Mn), % 0
1.0 to 2.5
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
19 to 21
Niobium (Nb), % 2.0 to 3.0
0.75 to 1.3
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
2.0 to 3.0
Zirconium (Zr), % 91 to 98
0