R60706 Alloy vs. Grade 7 Babbitt Metal

Both R60706 alloy and grade 7 Babbitt Metal are otherwise unclassified metals. There are 12 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is grade 7 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
26
Poisson's Ratio 0.34
0.4
Shear Modulus, GPa 37
9.1
Tensile Strength: Yield (Proof), MPa 390
25

Thermal Properties

Latent Heat of Fusion, J/g 250
48
Specific Heat Capacity, J/kg-K 270
150
Thermal Expansion, µm/m-K 6.3
26

Otherwise Unclassified Properties

Density, g/cm3 6.7
10
Embodied Water, L/kg 450
880

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 760
12
Stiffness to Weight: Axial, points 8.1
1.4
Stiffness to Weight: Bending, points 23
9.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
14 to 16
Arsenic (As), % 0
0.3 to 0.6
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 0 to 0.2
0
Copper (Cu), % 0
0 to 0.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
0 to 0.1
Lead (Pb), % 0
71.9 to 76.4
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Tin (Sn), % 0
9.3 to 10.7
Zinc (Zn), % 0
0 to 0.0050
Zirconium (Zr), % 91 to 98
0