R60706 Alloy vs. Solder Alloy 122

Both R60706 alloy and solder alloy 122 are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is solder alloy 122.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
20
Elongation at Break, % 16
30
Poisson's Ratio 0.34
0.43
Shear Modulus, GPa 37
6.9
Tensile Strength: Ultimate (UTS), MPa 580
30

Thermal Properties

Latent Heat of Fusion, J/g 250
27
Specific Heat Capacity, J/kg-K 270
140
Thermal Conductivity, W/m-K 17
25
Thermal Expansion, µm/m-K 6.3
28

Otherwise Unclassified Properties

Density, g/cm3 6.7
11
Embodied Water, L/kg 450
540

Common Calculations

Stiffness to Weight: Axial, points 8.1
1.0
Stiffness to Weight: Bending, points 23
8.2
Strength to Weight: Axial, points 24
0.77
Strength to Weight: Bending, points 23
2.0
Thermal Diffusivity, mm2/s 9.5
17
Thermal Shock Resistance, points 67
3.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 0 to 0.2
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.2
0 to 0.020
Lead (Pb), % 0
88.4 to 90.5
Nickel (Ni), % 0
0 to 0.010
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
9.5 to 10.5
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 91 to 98
0