R60706 Alloy vs. Z41321 Zinc

R60706 alloy belongs to the otherwise unclassified metals classification, while Z41321 zinc belongs to the zinc alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is Z41321 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
87
Elongation at Break, % 16
60
Poisson's Ratio 0.34
0.25
Shear Modulus, GPa 37
35
Tensile Strength: Ultimate (UTS), MPa 580
190
Tensile Strength: Yield (Proof), MPa 390
150

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 17
110
Thermal Expansion, µm/m-K 6.3
26

Otherwise Unclassified Properties

Density, g/cm3 6.7
6.6
Embodied Water, L/kg 450
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
100
Resilience: Unit (Modulus of Resilience), kJ/m3 760
130
Stiffness to Weight: Axial, points 8.1
7.4
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 24
7.9
Strength to Weight: Bending, points 23
11
Thermal Diffusivity, mm2/s 9.5
44
Thermal Shock Resistance, points 67
5.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 0 to 0.2
0
Copper (Cu), % 0
0.5 to 1.0
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0.080 to 0.18
Zinc (Zn), % 0
98.8 to 99.42
Zirconium (Zr), % 91 to 98
0