R60802 Alloy vs. 206.0 Aluminum
R60802 alloy belongs to the otherwise unclassified metals classification, while 206.0 aluminum belongs to the aluminum alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is R60802 alloy and the bottom bar is 206.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 98 | |
71 |
Elongation at Break, % | 22 | |
8.4 to 12 |
Poisson's Ratio | 0.34 | |
0.33 |
Shear Modulus, GPa | 36 | |
27 |
Tensile Strength: Ultimate (UTS), MPa | 430 | |
330 to 440 |
Tensile Strength: Yield (Proof), MPa | 270 | |
190 to 350 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
390 |
Specific Heat Capacity, J/kg-K | 270 | |
880 |
Thermal Conductivity, W/m-K | 22 | |
120 |
Thermal Expansion, µm/m-K | 6.0 | |
19 |
Otherwise Unclassified Properties
Density, g/cm3 | 6.5 | |
3.0 |
Embodied Water, L/kg | 290 | |
1150 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 85 | |
24 to 49 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
270 to 840 |
Stiffness to Weight: Axial, points | 8.3 | |
13 |
Stiffness to Weight: Bending, points | 23 | |
46 |
Strength to Weight: Axial, points | 18 | |
30 to 40 |
Strength to Weight: Bending, points | 19 | |
35 to 42 |
Thermal Diffusivity, mm2/s | 12 | |
46 |
Thermal Shock Resistance, points | 53 | |
17 to 23 |
Alloy Composition
Aluminum (Al), % | 0 | |
93.3 to 95.3 |
Chromium (Cr), % | 0.050 to 0.15 | |
0 |
Copper (Cu), % | 0 | |
4.2 to 5.0 |
Iron (Fe), % | 0.070 to 0.2 | |
0 to 0.15 |
Magnesium (Mg), % | 0 | |
0.15 to 0.35 |
Manganese (Mn), % | 0 | |
0.2 to 0.5 |
Nickel (Ni), % | 0.030 to 0.080 | |
0 to 0.050 |
Silicon (Si), % | 0 | |
0 to 0.1 |
Tin (Sn), % | 1.2 to 1.7 | |
0 to 0.050 |
Titanium (Ti), % | 0 | |
0.15 to 0.3 |
Zinc (Zn), % | 0 | |
0 to 0.1 |
Zirconium (Zr), % | 97.8 to 98.7 | |
0 |
Residuals, % | 0 | |
0 to 0.15 |