R60802 Alloy vs. AWS BNi-7
R60802 alloy belongs to the otherwise unclassified metals classification, while AWS BNi-7 belongs to the nickel alloys. There are 14 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is R60802 alloy and the bottom bar is AWS BNi-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 170 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Shear Modulus, GPa | 36 | |
| 67 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 490 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.5 | |
| 8.0 |
| Embodied Water, L/kg | 290 | |
| 240 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.3 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 18 | |
| 19 |
| Strength to Weight: Bending, points | 19 | |
| 19 |
| Thermal Shock Resistance, points | 53 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Boron (B), % | 0 | |
| 0 to 0.010 |
| Carbon (C), % | 0 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0.050 to 0.15 | |
| 13 to 15 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0.070 to 0.2 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 | |
| 0 to 0.040 |
| Nickel (Ni), % | 0.030 to 0.080 | |
| 73.3 to 77.3 |
| Phosphorus (P), % | 0 | |
| 9.7 to 10.5 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 1.2 to 1.7 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 97.8 to 98.7 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.11 | |
| 0 to 0.5 |