R60802 Alloy vs. Z40301 Zinc
R60802 alloy belongs to the otherwise unclassified metals classification, while Z40301 zinc belongs to the zinc alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R60802 alloy and the bottom bar is Z40301 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 98 | |
87 |
Elongation at Break, % | 22 | |
60 |
Poisson's Ratio | 0.34 | |
0.25 |
Shear Modulus, GPa | 36 | |
35 |
Tensile Strength: Ultimate (UTS), MPa | 430 | |
190 |
Tensile Strength: Yield (Proof), MPa | 270 | |
150 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
110 |
Specific Heat Capacity, J/kg-K | 270 | |
390 |
Thermal Conductivity, W/m-K | 22 | |
110 |
Thermal Expansion, µm/m-K | 6.0 | |
26 |
Otherwise Unclassified Properties
Density, g/cm3 | 6.5 | |
6.6 |
Embodied Water, L/kg | 290 | |
340 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 85 | |
100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
130 |
Stiffness to Weight: Axial, points | 8.3 | |
7.4 |
Stiffness to Weight: Bending, points | 23 | |
23 |
Strength to Weight: Axial, points | 18 | |
7.9 |
Strength to Weight: Bending, points | 19 | |
11 |
Thermal Diffusivity, mm2/s | 12 | |
44 |
Thermal Shock Resistance, points | 53 | |
5.9 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.010 |
Cadmium (Cd), % | 0 | |
0 to 0.0050 |
Chromium (Cr), % | 0.050 to 0.15 | |
0 |
Copper (Cu), % | 0 | |
0.5 to 1.0 |
Iron (Fe), % | 0.070 to 0.2 | |
0 to 0.010 |
Lead (Pb), % | 0 | |
0 to 0.010 |
Nickel (Ni), % | 0.030 to 0.080 | |
0 |
Tin (Sn), % | 1.2 to 1.7 | |
0 to 0.0030 |
Titanium (Ti), % | 0 | |
0 to 0.040 |
Zinc (Zn), % | 0 | |
98.9 to 99.5 |
Zirconium (Zr), % | 97.8 to 98.7 | |
0 |
Residuals, % | 0 to 0.11 | |
0 |