R60802 Alloy vs. Z41121 Zinc

R60802 alloy belongs to the otherwise unclassified metals classification, while Z41121 zinc belongs to the zinc alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is R60802 alloy and the bottom bar is Z41121 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
87
Elongation at Break, % 22
50
Poisson's Ratio 0.34
0.25
Shear Modulus, GPa 36
35
Tensile Strength: Ultimate (UTS), MPa 430
140
Tensile Strength: Yield (Proof), MPa 270
120

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 22
110
Thermal Expansion, µm/m-K 6.0
26

Otherwise Unclassified Properties

Density, g/cm3 6.5
6.6
Embodied Water, L/kg 290
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 85
68
Resilience: Unit (Modulus of Resilience), kJ/m3 380
79
Stiffness to Weight: Axial, points 8.3
7.4
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 18
6.1
Strength to Weight: Bending, points 19
9.3
Thermal Diffusivity, mm2/s 12
44
Thermal Shock Resistance, points 53
4.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Chromium (Cr), % 0.050 to 0.15
0
Copper (Cu), % 0
0.080 to 0.49
Iron (Fe), % 0.070 to 0.2
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Nickel (Ni), % 0.030 to 0.080
0
Tin (Sn), % 1.2 to 1.7
0 to 0.0030
Titanium (Ti), % 0
0.050 to 0.18
Zinc (Zn), % 0
99.292 to 99.87
Zirconium (Zr), % 97.8 to 98.7
0
Residuals, % 0 to 0.11
0