Both R60804 alloy and AWS BAu-5 are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R60804 alloy and the bottom bar is AWS BAu-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
140
Poisson's Ratio 0.34
0.37
Shear Modulus, GPa 36
50
Tensile Strength: Ultimate (UTS), MPa 430
210

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Specific Heat Capacity, J/kg-K 270
280
Thermal Expansion, µm/m-K 6.0
12

Otherwise Unclassified Properties

Density, g/cm3 6.5
13

Common Calculations

Stiffness to Weight: Axial, points 8.3
5.8
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 18
4.5
Strength to Weight: Bending, points 19
6.0
Thermal Shock Resistance, points 53
9.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Chromium (Cr), % 0.070 to 0.13
0
Gold (Au), % 0
29.5 to 30.5
Iron (Fe), % 0.18 to 0.24
0
Nickel (Ni), % 0
35.5 to 36.4
Palladium (Pd), % 0
33.5 to 34.5
Tin (Sn), % 1.2 to 1.7
0
Zirconium (Zr), % 97.8 to 98.6
0
Residuals, % 0 to 0.12
0 to 0.15