Both R60804 alloy and AWS BVAu-4 are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R60804 alloy and the bottom bar is AWS BVAu-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
110
Poisson's Ratio 0.34
0.4
Shear Modulus, GPa 36
41
Tensile Strength: Ultimate (UTS), MPa 430
190

Thermal Properties

Latent Heat of Fusion, J/g 250
100
Specific Heat Capacity, J/kg-K 270
190
Thermal Expansion, µm/m-K 6.0
14

Otherwise Unclassified Properties

Density, g/cm3 6.5
17

Common Calculations

Stiffness to Weight: Axial, points 8.3
3.6
Stiffness to Weight: Bending, points 23
9.3
Strength to Weight: Axial, points 18
3.0
Strength to Weight: Bending, points 19
4.2
Thermal Shock Resistance, points 53
8.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0
0 to 0.0050
Chromium (Cr), % 0.070 to 0.13
0
Gold (Au), % 0
81.5 to 82.5
Iron (Fe), % 0.18 to 0.24
0
Lead (Pb), % 0
0 to 0.0020
Nickel (Ni), % 0
17.5 to 18.5
Phosphorus (P), % 0
0 to 0.0020
Tin (Sn), % 1.2 to 1.7
0
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 97.8 to 98.6
0
Residuals, % 0 to 0.12
0