R60804 Alloy vs. Solder Alloy 123

Both R60804 alloy and solder alloy 123 are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60804 alloy and the bottom bar is solder alloy 123.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
18
Elongation at Break, % 22
45
Poisson's Ratio 0.34
0.44
Shear Modulus, GPa 36
6.2
Tensile Strength: Ultimate (UTS), MPa 430
28

Thermal Properties

Latent Heat of Fusion, J/g 250
26
Specific Heat Capacity, J/kg-K 270
130
Thermal Conductivity, W/m-K 22
23
Thermal Expansion, µm/m-K 6.0
29

Otherwise Unclassified Properties

Density, g/cm3 6.5
11
Embodied Water, L/kg 290
500

Common Calculations

Stiffness to Weight: Axial, points 8.3
0.9
Stiffness to Weight: Bending, points 23
7.8
Strength to Weight: Axial, points 18
0.69
Strength to Weight: Bending, points 19
1.8
Thermal Diffusivity, mm2/s 12
16
Thermal Shock Resistance, points 53
3.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0050
Chromium (Cr), % 0.070 to 0.13
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0.18 to 0.24
0 to 0.020
Lead (Pb), % 0
93.5 to 95.5
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 1.2 to 1.7
4.5 to 5.5
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 97.8 to 98.6
0
Residuals, % 0 to 0.12
0