R60901 Alloy vs. ASTM A210 Steel
R60901 alloy belongs to the otherwise unclassified metals classification, while ASTM A210 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is R60901 alloy and the bottom bar is ASTM A210 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 98 | |
190 |
Elongation at Break, % | 17 to 22 | |
34 |
Poisson's Ratio | 0.34 | |
0.29 |
Shear Modulus, GPa | 37 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 500 to 580 | |
470 to 540 |
Tensile Strength: Yield (Proof), MPa | 350 to 390 | |
290 to 310 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Specific Heat Capacity, J/kg-K | 270 | |
470 |
Thermal Conductivity, W/m-K | 17 | |
52 to 53 |
Thermal Expansion, µm/m-K | 6.3 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 6.6 | |
7.9 |
Embodied Water, L/kg | 270 | |
45 to 46 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 88 to 100 | |
140 to 160 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 640 to 760 | |
230 to 250 |
Stiffness to Weight: Axial, points | 8.3 | |
13 |
Stiffness to Weight: Bending, points | 23 | |
24 |
Strength to Weight: Axial, points | 21 to 25 | |
17 to 19 |
Strength to Weight: Bending, points | 21 to 24 | |
17 to 19 |
Thermal Diffusivity, mm2/s | 9.7 | |
14 |
Thermal Shock Resistance, points | 58 to 67 | |
15 to 17 |