R60901 Alloy vs. AWS BAg-13

Both R60901 alloy and AWS BAg-13 are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60901 alloy and the bottom bar is AWS BAg-13.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
91
Poisson's Ratio 0.34
0.35
Shear Modulus, GPa 37
34
Tensile Strength: Ultimate (UTS), MPa 500 to 580
180

Thermal Properties

Latent Heat of Fusion, J/g 250
150
Specific Heat Capacity, J/kg-K 270
310
Thermal Expansion, µm/m-K 6.3
19

Otherwise Unclassified Properties

Density, g/cm3 6.6
9.7

Common Calculations

Stiffness to Weight: Axial, points 8.3
5.2
Stiffness to Weight: Bending, points 23
16
Strength to Weight: Axial, points 21 to 25
5.2
Strength to Weight: Bending, points 21 to 24
7.3
Thermal Shock Resistance, points 58 to 67
7.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 0
37.4 to 42.5
Nickel (Ni), % 0
0.5 to 1.5
Niobium (Nb), % 2.4 to 2.8
0
Silver (Ag), % 0
53 to 55
Zinc (Zn), % 0
4.0 to 6.0
Zirconium (Zr), % 96.8 to 97.5
0
Residuals, % 0 to 0.29
0 to 0.15