R60901 Alloy vs. Grade 15 Babbitt Metal
Both R60901 alloy and grade 15 Babbitt Metal are otherwise unclassified metals. There are 10 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is R60901 alloy and the bottom bar is grade 15 Babbitt Metal.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 6.6 | |
| 10 |
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 23 |
| Embodied Water, L/kg | 270 | |
| 840 |
| Latent Heat of Fusion, J/g | 250 | |
| 46 |
| Poisson's Ratio | 0.34 | |
| 0.4 |
| Shear Modulus, GPa | 37 | |
| 8.2 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 140 |
| Stiffness to Weight: Axial, points | 8.3 | |
| 1.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 9.0 |
| Thermal Expansion, µm/m-K | 6.3 | |
| 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 14.5 to 17.5 |
| Arsenic (As), % | 0 | |
| 0.8 to 1.4 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 0 to 0.6 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 79 to 83.9 |
| Niobium (Nb), % | 2.4 to 2.8 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.8 to 1.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Zirconium (Zr), % | 96.8 to 97.5 | |
| 0 |
| Residuals, % | 0 to 0.29 | |
| 0 |