R60901 Alloy vs. Grade 8 Babbitt Metal

Both R60901 alloy and grade 8 Babbitt Metal are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60901 alloy and the bottom bar is grade 8 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
24
Poisson's Ratio 0.34
0.41
Shear Modulus, GPa 37
8.5
Tensile Strength: Yield (Proof), MPa 350 to 390
23

Thermal Properties

Latent Heat of Fusion, J/g 250
46
Specific Heat Capacity, J/kg-K 270
150
Thermal Conductivity, W/m-K 17
24
Thermal Expansion, µm/m-K 6.3
24

Otherwise Unclassified Properties

Density, g/cm3 6.6
10
Embodied Water, L/kg 270
840

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 640 to 760
11
Stiffness to Weight: Axial, points 8.3
1.3
Stiffness to Weight: Bending, points 23
9.2
Thermal Diffusivity, mm2/s 9.7
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
14 to 16
Arsenic (As), % 0
0.3 to 0.6
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.050
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0
77.1 to 81.2
Niobium (Nb), % 2.4 to 2.8
0
Tin (Sn), % 0
4.5 to 5.5
Zinc (Zn), % 0
0 to 0.0050
Zirconium (Zr), % 96.8 to 97.5
0
Residuals, % 0 to 0.29
0