R60901 Alloy vs. Type 2 Pewter
Both R60901 alloy and Type 2 pewter are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is R60901 alloy and the bottom bar is Type 2 pewter.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 52 |
| Poisson's Ratio | 0.34 | |
| 0.35 |
| Shear Modulus, GPa | 37 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 580 | |
| 52 to 68 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 69 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 220 |
| Thermal Expansion, µm/m-K | 6.3 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.6 | |
| 7.3 |
| Embodied Water, L/kg | 270 | |
| 1220 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.3 | |
| 3.9 |
| Stiffness to Weight: Bending, points | 23 | |
| 17 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 2.0 to 2.6 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 4.3 to 5.1 |
| Thermal Shock Resistance, points | 58 to 67 | |
| 3.4 to 4.4 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0 | |
| 5.0 to 7.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 0 | |
| 0 to 0.015 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Niobium (Nb), % | 2.4 to 2.8 | |
| 0 |
| Tin (Sn), % | 0 | |
| 90 to 93 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Zirconium (Zr), % | 96.8 to 97.5 | |
| 0 |
| Residuals, % | 0 to 0.29 | |
| 0 |