R60901 Alloy vs. K93600 Alloy
R60901 alloy belongs to the otherwise unclassified metals classification, while K93600 alloy belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is R60901 alloy and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 98 | |
140 |
Elongation at Break, % | 17 to 22 | |
5.0 to 35 |
Tensile Strength: Ultimate (UTS), MPa | 500 to 580 | |
480 to 810 |
Tensile Strength: Yield (Proof), MPa | 350 to 390 | |
280 to 750 |
Thermal Properties
Specific Heat Capacity, J/kg-K | 270 | |
520 |
Thermal Conductivity, W/m-K | 17 | |
13 |
Thermal Expansion, µm/m-K | 6.3 | |
7.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 6.6 | |
8.1 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 88 to 100 | |
21 to 280 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 640 to 760 | |
280 to 2050 |
Stiffness to Weight: Axial, points | 8.3 | |
9.4 |
Stiffness to Weight: Bending, points | 23 | |
21 |
Strength to Weight: Axial, points | 21 to 25 | |
16 to 28 |
Strength to Weight: Bending, points | 21 to 24 | |
17 to 24 |
Thermal Diffusivity, mm2/s | 9.7 | |
3.1 |
Thermal Shock Resistance, points | 58 to 67 | |
34 to 57 |