R60901 Alloy vs. N06002 Nickel

R60901 alloy belongs to the otherwise unclassified metals classification, while N06002 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R60901 alloy and the bottom bar is N06002 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
210
Elongation at Break, % 17 to 22
41
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
81
Tensile Strength: Ultimate (UTS), MPa 500 to 580
760
Tensile Strength: Yield (Proof), MPa 350 to 390
310

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Specific Heat Capacity, J/kg-K 270
450
Thermal Conductivity, W/m-K 17
9.9
Thermal Expansion, µm/m-K 6.3
14

Otherwise Unclassified Properties

Density, g/cm3 6.6
8.5
Embodied Water, L/kg 270
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88 to 100
250
Resilience: Unit (Modulus of Resilience), kJ/m3 640 to 760
230
Stiffness to Weight: Axial, points 8.3
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 21 to 25
25
Strength to Weight: Bending, points 21 to 24
22
Thermal Diffusivity, mm2/s 9.7
2.6
Thermal Shock Resistance, points 58 to 67
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
20.5 to 23
Cobalt (Co), % 0
0.5 to 2.5
Iron (Fe), % 0
17 to 20
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
42.3 to 54
Niobium (Nb), % 2.4 to 2.8
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
0.2 to 1.0
Zirconium (Zr), % 96.8 to 97.5
0
Residuals, % 0 to 0.29
0