S20432 Stainless Steel vs. AISI 201LN Stainless Steel

Both S20432 stainless steel and AISI 201LN stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is AISI 201LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
210 to 320
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
25 to 51
Fatigue Strength, MPa 210
340 to 540
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 400
530 to 680
Tensile Strength: Ultimate (UTS), MPa 580
740 to 1060
Tensile Strength: Yield (Proof), MPa 230
350 to 770

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 900
880
Melting Completion (Liquidus), °C 1410
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.6
Embodied Energy, MJ/kg 38
38
Embodied Water, L/kg 140
140

Common Calculations

PREN (Pitting Resistance) 20
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
230 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 140
310 to 1520
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
27 to 38
Strength to Weight: Bending, points 20
24 to 30
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 13
16 to 23

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 17 to 18
16 to 17.5
Copper (Cu), % 2.0 to 3.0
0 to 1.0
Iron (Fe), % 66.7 to 74
67.9 to 73.5
Manganese (Mn), % 3.0 to 5.0
6.4 to 7.5
Nickel (Ni), % 4.0 to 6.0
4.0 to 5.0
Nitrogen (N), % 0.050 to 0.2
0.1 to 0.25
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.015