S20432 Stainless Steel vs. AISI 305 Stainless Steel

Both S20432 stainless steel and AISI 305 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is AISI 305 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170 to 220
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
34 to 45
Fatigue Strength, MPa 210
210 to 280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 400
400 to 470
Tensile Strength: Ultimate (UTS), MPa 580
580 to 710
Tensile Strength: Yield (Proof), MPa 230
230 to 350

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 900
540
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
3.2
Embodied Energy, MJ/kg 38
45
Embodied Water, L/kg 140
150

Common Calculations

PREN (Pitting Resistance) 20
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
200 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 140
130 to 320
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
20 to 25
Strength to Weight: Bending, points 20
20 to 23
Thermal Diffusivity, mm2/s 4.0
4.2
Thermal Shock Resistance, points 13
13 to 15

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 17 to 18
17 to 19
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
65.1 to 72.5
Manganese (Mn), % 3.0 to 5.0
0 to 2.0
Nickel (Ni), % 4.0 to 6.0
10.5 to 13
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030