S20432 Stainless Steel vs. ASTM A369 Grade FP92

Both S20432 stainless steel and ASTM A369 grade FP92 are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is ASTM A369 grade FP92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
19
Fatigue Strength, MPa 210
330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 400
440
Tensile Strength: Ultimate (UTS), MPa 580
710
Tensile Strength: Yield (Proof), MPa 230
490

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 900
590
Melting Completion (Liquidus), °C 1410
1490
Melting Onset (Solidus), °C 1370
1450
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
26
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
10

Otherwise Unclassified Properties

Base Metal Price, % relative 13
11
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
2.8
Embodied Energy, MJ/kg 38
40
Embodied Water, L/kg 140
89

Common Calculations

PREN (Pitting Resistance) 20
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
620
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 4.0
6.9
Thermal Shock Resistance, points 13
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0 to 0.080
0.070 to 0.13
Chromium (Cr), % 17 to 18
8.5 to 9.5
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
85.8 to 89.1
Manganese (Mn), % 3.0 to 5.0
0.3 to 0.6
Molybdenum (Mo), % 0
0.3 to 0.6
Nickel (Ni), % 4.0 to 6.0
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0.050 to 0.2
0.030 to 0.070
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010