S20432 Stainless Steel vs. ASTM A572 Steel

Both S20432 stainless steel and ASTM A572 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is ASTM A572 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
140 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
18 to 25
Fatigue Strength, MPa 210
240 to 340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
300 to 380
Tensile Strength: Ultimate (UTS), MPa 580
470 to 620
Tensile Strength: Yield (Proof), MPa 230
330 to 510

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.2 to 8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.6
Embodied Energy, MJ/kg 38
22
Embodied Water, L/kg 140
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
100 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
290 to 690
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17 to 22
Strength to Weight: Bending, points 20
17 to 21
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
14 to 18