S20432 Stainless Steel vs. AWS ER80S-D2

Both S20432 stainless steel and AWS ER80S-D2 are iron alloys. They have 73% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is AWS ER80S-D2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 230
540

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
47
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.6
Embodied Energy, MJ/kg 38
21
Embodied Water, L/kg 140
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
770
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
22
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 13
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0.070 to 0.12
Chromium (Cr), % 17 to 18
0
Copper (Cu), % 2.0 to 3.0
0 to 0.5
Iron (Fe), % 66.7 to 74
95.2 to 97.4
Manganese (Mn), % 3.0 to 5.0
1.6 to 2.1
Molybdenum (Mo), % 0
0.4 to 0.6
Nickel (Ni), % 4.0 to 6.0
0 to 0.15
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0.5 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025
Residuals, % 0
0 to 0.5