S20432 Stainless Steel vs. EN 1.0562 Steel

Both S20432 stainless steel and EN 1.0562 steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.0562 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
24
Fatigue Strength, MPa 210
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
350
Tensile Strength: Ultimate (UTS), MPa 580
550
Tensile Strength: Yield (Proof), MPa 230
370

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
50
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.6
Embodied Energy, MJ/kg 38
22
Embodied Water, L/kg 140
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.080
0 to 0.18
Chromium (Cr), % 17 to 18
0 to 0.3
Copper (Cu), % 2.0 to 3.0
0 to 0.3
Iron (Fe), % 66.7 to 74
96.2 to 98.9
Manganese (Mn), % 3.0 to 5.0
1.1 to 1.7
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 4.0 to 6.0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.050 to 0.2
0 to 0.012
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.1