S20432 Stainless Steel vs. EN 1.4005 Stainless Steel

Both S20432 stainless steel and EN 1.4005 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4005 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
13 to 21
Fatigue Strength, MPa 210
240 to 290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 400
390 to 450
Tensile Strength: Ultimate (UTS), MPa 580
630 to 750
Tensile Strength: Yield (Proof), MPa 230
370 to 500

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Corrosion, °C 410
390
Maximum Temperature: Mechanical, °C 900
760
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.0
Embodied Energy, MJ/kg 38
28
Embodied Water, L/kg 140
100

Common Calculations

PREN (Pitting Resistance) 20
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
350 to 650
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
23 to 27
Strength to Weight: Bending, points 20
21 to 24
Thermal Diffusivity, mm2/s 4.0
8.1
Thermal Shock Resistance, points 13
23 to 27

Alloy Composition

Carbon (C), % 0 to 0.080
0.060 to 0.15
Chromium (Cr), % 17 to 18
12 to 14
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
82.4 to 87.8
Manganese (Mn), % 3.0 to 5.0
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.6
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0.15 to 0.35