S20432 Stainless Steel vs. EN 1.4016 Stainless Steel

Both S20432 stainless steel and EN 1.4016 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 88% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4016 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
22
Fatigue Strength, MPa 210
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 400
330
Tensile Strength: Ultimate (UTS), MPa 580
520
Tensile Strength: Yield (Proof), MPa 230
290

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 900
870
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
8.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.1
Embodied Energy, MJ/kg 38
29
Embodied Water, L/kg 140
120

Common Calculations

PREN (Pitting Resistance) 20
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
95
Resilience: Unit (Modulus of Resilience), kJ/m3 140
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.0
6.7
Thermal Shock Resistance, points 13
19

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.080
Chromium (Cr), % 17 to 18
16 to 18
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
79.9 to 84
Manganese (Mn), % 3.0 to 5.0
0 to 1.0
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015