S20432 Stainless Steel vs. EN 1.4439 Stainless Steel

Both S20432 stainless steel and EN 1.4439 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4439 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
40
Fatigue Strength, MPa 210
270
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Shear Strength, MPa 400
470
Tensile Strength: Ultimate (UTS), MPa 580
680
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 900
980
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
4.5
Embodied Energy, MJ/kg 38
61
Embodied Water, L/kg 140
160

Common Calculations

PREN (Pitting Resistance) 20
35
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
220
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 4.0
3.8
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 17 to 18
16.5 to 18.5
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
58.7 to 66.9
Manganese (Mn), % 3.0 to 5.0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 4.0 to 6.0
12.5 to 14.5
Nitrogen (N), % 0.050 to 0.2
0.12 to 0.22
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015