S20432 Stainless Steel vs. EN 1.4584 Stainless Steel

Both S20432 stainless steel and EN 1.4584 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4584 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
34
Fatigue Strength, MPa 210
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 580
500
Tensile Strength: Yield (Proof), MPa 230
210

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 17
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
31
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 2.7
5.7
Embodied Energy, MJ/kg 38
78
Embodied Water, L/kg 140
200

Common Calculations

PREN (Pitting Resistance) 20
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 4.0
4.5
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.025
Chromium (Cr), % 17 to 18
19 to 21
Copper (Cu), % 2.0 to 3.0
1.0 to 3.0
Iron (Fe), % 66.7 to 74
41.7 to 52
Manganese (Mn), % 3.0 to 5.0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 4.0 to 6.0
24 to 26
Nitrogen (N), % 0.050 to 0.2
0 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020