S20432 Stainless Steel vs. EN 1.4606 Stainless Steel

Both S20432 stainless steel and EN 1.4606 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4606 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
23 to 39
Fatigue Strength, MPa 210
240 to 420
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
75
Shear Strength, MPa 400
410 to 640
Tensile Strength: Ultimate (UTS), MPa 580
600 to 1020
Tensile Strength: Yield (Proof), MPa 230
280 to 630

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
770
Maximum Temperature: Mechanical, °C 900
910
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1370
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
26
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
6.0
Embodied Energy, MJ/kg 38
87
Embodied Water, L/kg 140
170

Common Calculations

PREN (Pitting Resistance) 20
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
190 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 140
200 to 1010
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
21 to 36
Strength to Weight: Bending, points 20
20 to 28
Thermal Diffusivity, mm2/s 4.0
3.7
Thermal Shock Resistance, points 13
21 to 35

Alloy Composition

Aluminum (Al), % 0
0 to 0.35
Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.080
0 to 0.080
Chromium (Cr), % 17 to 18
13 to 16
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
49.2 to 59
Manganese (Mn), % 3.0 to 5.0
1.0 to 2.0
Molybdenum (Mo), % 0
1.0 to 1.5
Nickel (Ni), % 4.0 to 6.0
24 to 27
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
1.9 to 2.3
Vanadium (V), % 0
0.1 to 0.5