S20432 Stainless Steel vs. EN 1.4823 Stainless Steel

Both S20432 stainless steel and EN 1.4823 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4823 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
3.4
Fatigue Strength, MPa 210
130
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 230
290

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1410
1400
Melting Onset (Solidus), °C 1370
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
16
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 2.7
3.0
Embodied Energy, MJ/kg 38
43
Embodied Water, L/kg 140
170

Common Calculations

PREN (Pitting Resistance) 20
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
17
Resilience: Unit (Modulus of Resilience), kJ/m3 140
200
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.0
4.5
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.080
0.3 to 0.5
Chromium (Cr), % 17 to 18
25 to 28
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
60.9 to 70.7
Manganese (Mn), % 3.0 to 5.0
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 4.0 to 6.0
3.0 to 6.0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030