S20432 Stainless Steel vs. EN 1.4845 Stainless Steel

Both S20432 stainless steel and EN 1.4845 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4845 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
38
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
78
Shear Strength, MPa 400
410
Tensile Strength: Ultimate (UTS), MPa 580
600
Tensile Strength: Yield (Proof), MPa 230
240

Thermal Properties

Latent Heat of Fusion, J/g 280
310
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 900
1050
Melting Completion (Liquidus), °C 1410
1400
Melting Onset (Solidus), °C 1370
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
4.3
Embodied Energy, MJ/kg 38
61
Embodied Water, L/kg 140
190

Common Calculations

PREN (Pitting Resistance) 20
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
180
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.1
Chromium (Cr), % 17 to 18
24 to 26
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
48.2 to 57
Manganese (Mn), % 3.0 to 5.0
0 to 2.0
Nickel (Ni), % 4.0 to 6.0
19 to 22
Nitrogen (N), % 0.050 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.015