MakeItFrom.com
Menu (ESC)

S20432 Stainless Steel vs. EN 1.4887 Stainless Steel

Both S20432 stainless steel and EN 1.4887 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.4887 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
45
Fatigue Strength, MPa 210
280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 400
400
Tensile Strength: Ultimate (UTS), MPa 580
580
Tensile Strength: Yield (Proof), MPa 230
300

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Corrosion, °C 410
600
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1410
1390
Melting Onset (Solidus), °C 1370
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 17
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
39
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.7
6.7
Embodied Energy, MJ/kg 38
96
Embodied Water, L/kg 140
210

Common Calculations

PREN (Pitting Resistance) 20
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
220
Resilience: Unit (Modulus of Resilience), kJ/m3 140
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.0
3.2
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.15
Chromium (Cr), % 17 to 18
20 to 23
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
34.2 to 45
Manganese (Mn), % 3.0 to 5.0
0 to 2.0
Nickel (Ni), % 4.0 to 6.0
33 to 37
Niobium (Nb), % 0
1.0 to 1.5
Nitrogen (N), % 0.050 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015