S20432 Stainless Steel vs. SAE-AISI 1042 Steel

Both S20432 stainless steel and SAE-AISI 1042 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is SAE-AISI 1042 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180 to 200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
14 to 18
Fatigue Strength, MPa 210
230 to 370
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
380 to 420
Tensile Strength: Ultimate (UTS), MPa 580
620 to 700
Tensile Strength: Yield (Proof), MPa 230
340 to 580

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 38
18
Embodied Water, L/kg 140
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
87 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 140
320 to 900
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
22 to 25
Strength to Weight: Bending, points 20
21 to 22
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
20 to 22

Alloy Composition

Carbon (C), % 0 to 0.080
0.4 to 0.47
Chromium (Cr), % 17 to 18
0
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
98.5 to 99
Manganese (Mn), % 3.0 to 5.0
0.6 to 0.9
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050