S20432 Stainless Steel vs. SAE-AISI 6150 Steel

Both S20432 stainless steel and SAE-AISI 6150 steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is SAE-AISI 6150 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200 to 350
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
15 to 23
Fatigue Strength, MPa 210
300 to 750
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
400 to 730
Tensile Strength: Ultimate (UTS), MPa 580
630 to 1200
Tensile Strength: Yield (Proof), MPa 230
420 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
420
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
46
Thermal Expansion, µm/m-K 17
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
2.0
Embodied Energy, MJ/kg 38
28
Embodied Water, L/kg 140
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
130 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 140
460 to 3590
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
22 to 43
Strength to Weight: Bending, points 20
21 to 32
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 13
20 to 38

Alloy Composition

Carbon (C), % 0 to 0.080
0.48 to 0.53
Chromium (Cr), % 17 to 18
0.8 to 1.1
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
96.7 to 97.7
Manganese (Mn), % 3.0 to 5.0
0.7 to 0.9
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040
Vanadium (V), % 0
0.15 to 0.3