S20432 Stainless Steel vs. N08028 Stainless Steel

Both S20432 stainless steel and N08028 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 60% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is N08028 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
45
Fatigue Strength, MPa 210
220
Poisson's Ratio 0.28
0.28
Rockwell B Hardness 81
80
Shear Modulus, GPa 76
80
Shear Strength, MPa 400
400
Tensile Strength: Ultimate (UTS), MPa 580
570
Tensile Strength: Yield (Proof), MPa 230
240

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Corrosion, °C 410
460
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1410
1420
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 17
16

Otherwise Unclassified Properties

Base Metal Price, % relative 13
37
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 2.7
6.4
Embodied Energy, MJ/kg 38
89
Embodied Water, L/kg 140
240

Common Calculations

PREN (Pitting Resistance) 20
39
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
210
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.0
3.2
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 17 to 18
26 to 28
Copper (Cu), % 2.0 to 3.0
0.6 to 1.4
Iron (Fe), % 66.7 to 74
29 to 40.4
Manganese (Mn), % 3.0 to 5.0
0 to 2.5
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 4.0 to 6.0
30 to 34
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030