S20432 Stainless Steel vs. S35500 Stainless Steel

Both S20432 stainless steel and S35500 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is S35500 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
14
Fatigue Strength, MPa 210
690 to 730
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 400
810 to 910
Tensile Strength: Ultimate (UTS), MPa 580
1330 to 1490
Tensile Strength: Yield (Proof), MPa 230
1200 to 1280

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 410
440
Maximum Temperature: Mechanical, °C 900
870
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
3.5
Embodied Energy, MJ/kg 38
47
Embodied Water, L/kg 140
130

Common Calculations

PREN (Pitting Resistance) 20
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
180 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 140
3610 to 4100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
47 to 53
Strength to Weight: Bending, points 20
34 to 37
Thermal Diffusivity, mm2/s 4.0
4.4
Thermal Shock Resistance, points 13
44 to 49

Alloy Composition

Carbon (C), % 0 to 0.080
0.1 to 0.15
Chromium (Cr), % 17 to 18
15 to 16
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
73.2 to 77.7
Manganese (Mn), % 3.0 to 5.0
0.5 to 1.3
Molybdenum (Mo), % 0
2.5 to 3.2
Nickel (Ni), % 4.0 to 6.0
4.0 to 5.0
Niobium (Nb), % 0
0.1 to 0.5
Nitrogen (N), % 0.050 to 0.2
0.070 to 0.13
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030