S21460 Stainless Steel vs. SAE-AISI H13 Steel

Both S21460 stainless steel and SAE-AISI H13 steel are iron alloys. They have 67% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S21460 stainless steel and the bottom bar is SAE-AISI H13 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 830
690 to 1820

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 18
10

Otherwise Unclassified Properties

Base Metal Price, % relative 14
6.0
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.0
4.3
Embodied Energy, MJ/kg 43
64
Embodied Water, L/kg 160
78

Common Calculations

PREN (Pitting Resistance) 25
9.9
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
25 to 65
Strength to Weight: Bending, points 26
22 to 43
Thermal Shock Resistance, points 17
25 to 65

Alloy Composition

Carbon (C), % 0 to 0.12
0.32 to 0.45
Chromium (Cr), % 17 to 19
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 57.3 to 63.7
88.8 to 92
Manganese (Mn), % 14 to 16
0.2 to 0.5
Molybdenum (Mo), % 0
1.1 to 1.8
Nickel (Ni), % 5.0 to 6.0
0 to 0.3
Nitrogen (N), % 0.35 to 0.5
0
Phosphorus (P), % 0 to 0.060
0 to 0.030
Silicon (Si), % 0 to 1.0
0.8 to 1.2
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.8 to 1.2