S21600 Stainless Steel vs. ASTM Grade LC2-1 Steel
Both S21600 stainless steel and ASTM grade LC2-1 steel are iron alloys. They have 69% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S21600 stainless steel and the bottom bar is ASTM grade LC2-1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 240 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 46 | |
| 20 |
| Fatigue Strength, MPa | 360 | |
| 430 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 56 | |
| 34 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 810 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 450 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 17 | |
| 5.0 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 1.9 |
| Embodied Energy, MJ/kg | 50 | |
| 25 |
| Embodied Water, L/kg | 160 | |
| 60 |
Common Calculations
| PREN (Pitting Resistance) | 34 | |
| 3.1 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 270 | |
| 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 1040 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 25 | |
| 29 |
| Strength to Weight: Bending, points | 23 | |
| 25 |
| Thermal Shock Resistance, points | 15 | |
| 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.22 |
| Chromium (Cr), % | 17.5 to 22 | |
| 1.4 to 1.9 |
| Iron (Fe), % | 57.6 to 67.8 | |
| 92.5 to 95.3 |
| Manganese (Mn), % | 7.5 to 9.0 | |
| 0.55 to 0.75 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 5.0 to 7.0 | |
| 2.5 to 3.5 |
| Nitrogen (N), % | 0.25 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.045 |