S30600 Stainless Steel vs. ACI-ASTM CD6MN Steel

Both S30600 stainless steel and ACI-ASTM CD6MN steel are iron alloys. They have 86% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is ACI-ASTM CD6MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 45
28
Fatigue Strength, MPa 250
370
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 610
730
Tensile Strength: Yield (Proof), MPa 270
510

Thermal Properties

Latent Heat of Fusion, J/g 350
300
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1380
1440
Melting Onset (Solidus), °C 1330
1390
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
17
Density, g/cm3 7.6
7.7
Embodied Carbon, kg CO2/kg material 3.6
3.4
Embodied Energy, MJ/kg 51
48
Embodied Water, L/kg 150
170

Common Calculations

PREN (Pitting Resistance) 18
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
180
Resilience: Unit (Modulus of Resilience), kJ/m3 190
650
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
26
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 3.7
4.4
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.060
Chromium (Cr), % 17 to 18.5
24 to 27
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
62.1 to 70.1
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.2
1.8 to 2.5
Nickel (Ni), % 14 to 15.5
4.0 to 6.0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 3.7 to 4.3
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.040