S30600 Stainless Steel vs. ACI-ASTM CH10 Steel

Both S30600 stainless steel and ACI-ASTM CH10 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is ACI-ASTM CH10 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 45
34
Fatigue Strength, MPa 250
180
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 610
540
Tensile Strength: Yield (Proof), MPa 270
230

Thermal Properties

Latent Heat of Fusion, J/g 350
310
Maximum Temperature: Corrosion, °C 410
440
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1380
1410
Melting Onset (Solidus), °C 1330
1370
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
20
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
3.7
Embodied Energy, MJ/kg 51
53
Embodied Water, L/kg 150
180

Common Calculations

PREN (Pitting Resistance) 18
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
150
Resilience: Unit (Modulus of Resilience), kJ/m3 190
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 3.7
3.9
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.1
Chromium (Cr), % 17 to 18.5
22 to 26
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
54.8 to 66
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.2
0 to 0.5
Nickel (Ni), % 14 to 15.5
12 to 15
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 3.7 to 4.3
0 to 2.0
Sulfur (S), % 0 to 0.020
0 to 0.040