S30600 Stainless Steel vs. ASTM A372 Grade G Steel

Both S30600 stainless steel and ASTM A372 grade G steel are iron alloys. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is ASTM A372 grade G steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200 to 280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 45
20 to 22
Fatigue Strength, MPa 250
310 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 430
410 to 570
Tensile Strength: Ultimate (UTS), MPa 610
650 to 910
Tensile Strength: Yield (Proof), MPa 270
430 to 550

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 950
410
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
46
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.2
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.5
Embodied Energy, MJ/kg 51
20
Embodied Water, L/kg 150
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
130 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 190
500 to 810
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
23 to 32
Strength to Weight: Bending, points 21
21 to 27
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 14
19 to 27

Alloy Composition

Carbon (C), % 0 to 0.018
0.25 to 0.35
Chromium (Cr), % 17 to 18.5
0.4 to 0.65
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
97.4 to 98.4
Manganese (Mn), % 0 to 2.0
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.2
0.15 to 0.25
Nickel (Ni), % 14 to 15.5
0
Phosphorus (P), % 0 to 0.020
0 to 0.015
Silicon (Si), % 3.7 to 4.3
0.15 to 0.35
Sulfur (S), % 0 to 0.020
0 to 0.010