S30600 Stainless Steel vs. ASTM Grade HF Steel

Both S30600 stainless steel and ASTM grade HF steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is ASTM grade HF steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 45
29
Fatigue Strength, MPa 250
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 610
550
Tensile Strength: Yield (Proof), MPa 270
270

Thermal Properties

Latent Heat of Fusion, J/g 350
300
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 950
1000
Melting Completion (Liquidus), °C 1380
1410
Melting Onset (Solidus), °C 1330
1370
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
17
Density, g/cm3 7.6
7.7
Embodied Carbon, kg CO2/kg material 3.6
3.2
Embodied Energy, MJ/kg 51
46
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 18
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
130
Resilience: Unit (Modulus of Resilience), kJ/m3 190
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 3.7
4.2
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0 to 0.018
0.2 to 0.4
Chromium (Cr), % 17 to 18.5
18 to 23
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
60 to 73.8
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.2
0 to 0.5
Nickel (Ni), % 14 to 15.5
8.0 to 12
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 3.7 to 4.3
0 to 2.0
Sulfur (S), % 0 to 0.020
0 to 0.040