S30600 Stainless Steel vs. AWS E410

Both S30600 stainless steel and AWS E410 are iron alloys. They have 76% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is AWS E410.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 45
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 610
580
Tensile Strength: Yield (Proof), MPa 270
440

Thermal Properties

Latent Heat of Fusion, J/g 350
270
Melting Completion (Liquidus), °C 1380
1450
Melting Onset (Solidus), °C 1330
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
28
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
7.5
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
2.0
Embodied Energy, MJ/kg 51
28
Embodied Water, L/kg 150
100

Common Calculations

PREN (Pitting Resistance) 18
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
120
Resilience: Unit (Modulus of Resilience), kJ/m3 190
500
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.7
7.5
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.12
Chromium (Cr), % 17 to 18.5
11 to 13.5
Copper (Cu), % 0 to 0.5
0 to 0.75
Iron (Fe), % 58.9 to 65.3
82.2 to 89
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.2
0 to 0.75
Nickel (Ni), % 14 to 15.5
0 to 0.7
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 3.7 to 4.3
0 to 0.9
Sulfur (S), % 0 to 0.020
0 to 0.030