S30600 Stainless Steel vs. EN 1.3519 Steel

Both S30600 stainless steel and EN 1.3519 steel are iron alloys. They have 65% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.3519 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 610
620 to 730

Thermal Properties

Latent Heat of Fusion, J/g 350
260
Maximum Temperature: Mechanical, °C 950
430
Melting Completion (Liquidus), °C 1380
1440
Melting Onset (Solidus), °C 1330
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
43
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.6
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.5
Embodied Energy, MJ/kg 51
21
Embodied Water, L/kg 150
55

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
22 to 26
Strength to Weight: Bending, points 21
21 to 23
Thermal Diffusivity, mm2/s 3.7
12
Thermal Shock Resistance, points 14
18 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.018
0.93 to 1.1
Chromium (Cr), % 17 to 18.5
1.4 to 1.7
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 58.9 to 65.3
95.4 to 96.8
Manganese (Mn), % 0 to 2.0
1.4 to 1.7
Molybdenum (Mo), % 0 to 0.2
0 to 0.1
Nickel (Ni), % 14 to 15.5
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 3.7 to 4.3
0.45 to 0.75
Sulfur (S), % 0 to 0.020
0 to 0.030