S30600 Stainless Steel vs. EN 1.4305 Stainless Steel

Both S30600 stainless steel and EN 1.4305 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.4305 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 45
14 to 40
Fatigue Strength, MPa 250
190 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 430
420 to 550
Tensile Strength: Ultimate (UTS), MPa 610
610 to 900
Tensile Strength: Yield (Proof), MPa 270
220 to 570

Thermal Properties

Latent Heat of Fusion, J/g 350
290
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 950
930
Melting Completion (Liquidus), °C 1380
1420
Melting Onset (Solidus), °C 1330
1380
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 19
15
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
3.0
Embodied Energy, MJ/kg 51
42
Embodied Water, L/kg 150
140

Common Calculations

PREN (Pitting Resistance) 18
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 190
120 to 830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
22 to 32
Strength to Weight: Bending, points 21
20 to 27
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 14
14 to 20

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.1
Chromium (Cr), % 17 to 18.5
17 to 19
Copper (Cu), % 0 to 0.5
0 to 1.0
Iron (Fe), % 58.9 to 65.3
66.4 to 74.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 14 to 15.5
8.0 to 10
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 3.7 to 4.3
0 to 1.0
Sulfur (S), % 0 to 0.020
0.15 to 0.35