S30600 Stainless Steel vs. EN 1.4317 Stainless Steel

Both S30600 stainless steel and EN 1.4317 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.4317 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 45
17
Fatigue Strength, MPa 250
380
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 610
860
Tensile Strength: Yield (Proof), MPa 270
630

Thermal Properties

Latent Heat of Fusion, J/g 350
280
Maximum Temperature: Corrosion, °C 410
390
Maximum Temperature: Mechanical, °C 950
770
Melting Completion (Liquidus), °C 1380
1440
Melting Onset (Solidus), °C 1330
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
26
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
10
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
2.4
Embodied Energy, MJ/kg 51
33
Embodied Water, L/kg 150
110

Common Calculations

PREN (Pitting Resistance) 18
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
130
Resilience: Unit (Modulus of Resilience), kJ/m3 190
1010
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
31
Strength to Weight: Bending, points 21
26
Thermal Diffusivity, mm2/s 3.7
7.0
Thermal Shock Resistance, points 14
30

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.060
Chromium (Cr), % 17 to 18.5
12 to 13.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
78.7 to 84.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.2
0 to 0.7
Nickel (Ni), % 14 to 15.5
3.5 to 5.0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 3.7 to 4.3
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.025