S30600 Stainless Steel vs. EN 1.4537 Stainless Steel

Both S30600 stainless steel and EN 1.4537 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.4537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
220
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 45
42
Fatigue Strength, MPa 250
290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Shear Strength, MPa 430
480
Tensile Strength: Ultimate (UTS), MPa 610
700
Tensile Strength: Yield (Proof), MPa 270
330

Thermal Properties

Latent Heat of Fusion, J/g 350
310
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1380
1440
Melting Onset (Solidus), °C 1330
1390
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
34
Density, g/cm3 7.6
8.1
Embodied Carbon, kg CO2/kg material 3.6
6.1
Embodied Energy, MJ/kg 51
84
Embodied Water, L/kg 150
220

Common Calculations

PREN (Pitting Resistance) 18
46
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
240
Resilience: Unit (Modulus of Resilience), kJ/m3 190
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 3.7
3.7
Thermal Shock Resistance, points 14
15

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.020
Chromium (Cr), % 17 to 18.5
24 to 26
Copper (Cu), % 0 to 0.5
1.0 to 2.0
Iron (Fe), % 58.9 to 65.3
36.3 to 46.1
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.2
4.7 to 5.7
Nickel (Ni), % 14 to 15.5
24 to 27
Nitrogen (N), % 0
0.17 to 0.25
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 3.7 to 4.3
0 to 0.7
Sulfur (S), % 0 to 0.020
0 to 0.010